Elastic polymer cement waterproofing material Teknomer 200 EX (30 kg)

Two-component, elastic polymer-cement waterproofing for positive water pressure

Teknomer 200 EX is a two-component, cement-based, polymer-reinforced waterproofing. Fully elastic, with special additives. It is used internally or externally on concrete monolithic and prefabricated reinforced concrete structures for waterproofing.

Areas of application

• On vertical and horizontal surfaces indoors and outdoors

• Swimming pools

• Water pits, fire tanks

• Drainage structures

• Reservoirs and decorative pools

• Terraces (with protection condition)

• Bathroom, toilets, bathrooms

• It is allowed to lay ceramic tiles and other finishing materials on the adhesive layer over the waterproofing.

Features and benefits

• Can be applied with a brush, a trowel or a sprayer.
• Does not shrink or crack, does not shrink.
• Can be applied to fresh screed and concrete surfaces due to its crack-bridging function.
• Prevents carbonation in concrete.
• Does not contain aggressive and toxic substances and can be used in drinking water tanks and indoors.
• Gives the concrete surface high resistance to the effects of salty sea water, phosphates and chlorides.

Recommendations for use

• Care must be taken not to damage the insulating material during the coating process.
• Do not apply to surfaces made of wood, metal, fiberboard, MDF, plywood, or PVC.
• Do not add other ingredients to the mixture.
• To achieve maximum protective characteristics, further work on the surface should be carried out no earlier than after 72 hours.
• After application, the surface should be protected from direct sunlight, strong wind, high (above + 35 ° C) and negative temperatures, and precipitation.
• Equipment should be rinsed with water immediately after application. Once the product has hardened, it can only be cleaned mechanically.

Instructions for use

20 kg of the powder solution should be gradually mixed with the liquid component, adding it slowly to avoid lumps. It is recommended to use a mixer with a low rotation speed (less than 500 rpm). After the initial mixing, the solution should be left to mature for 5 minutes, and then mixed again for 1-2 minutes immediately before application.

The finished solution is applied in two layers using a roller, brush or trowel. Between the layers, an interval of 5–6 hours must be maintained (depending on the ambient temperature). Each subsequent layer is applied perpendicular to the previous one. The total thickness of the application should be 2–3 mm.

FEATURES